| 1 | #Zirconium Silicide, ZrSi2 |
|---|
| 2 | #Structure Orthorhombic, Cmcm (63), Z = 4 [Seyfarth, 1928]. The structure was redetermined by Schachner |
|---|
| 3 | #et al. [1954] and by Vaughn and Bracuti [1958]. |
|---|
| 4 | #Lattice constants of this sample |
|---|
| 5 | #a = 3.6958(3), b = 14.7514(9), c = 3.6654(3) |
|---|
| 6 | #a/b = 0.2505, c/b = 0.2485 |
|---|
| 7 | #Volume 199.83 A3 |
|---|
| 8 | 7.37 |
|---|
| 9 | 3.685 |
|---|
| 10 | 3.586 |
|---|
| 11 | 3.283 |
|---|
| 12 | 2.954 |
|---|
| 13 | 2.601 |
|---|
| 14 | 2.564 |
|---|
| 15 | 2.458 |
|---|
| 16 | 2.300 |
|---|
| 17 | 2.0417 |
|---|
| 18 | 1.9518 |
|---|
| 19 | 1.8480 |
|---|
| 20 | 1.8434 |
|---|
| 21 | 1.8330 |
|---|
| 22 | 1.7782 |
|---|
| 23 | 1.6519 |
|---|
| 24 | 1.6473 |
|---|
| 25 | 1.6381 |
|---|
| 26 | 1.6322 |
|---|
| 27 | 1.6102 |
|---|
| 28 | 1.5576 |
|---|
| 29 | 1.4982 |
|---|
| 30 | 1.4772 |
|---|
| 31 | 1.4692 |
|---|
| 32 | 1.4346 |
|---|
| 33 | 1.3867 |
|---|
| 34 | 1.3704 |
|---|
| 35 | 1.3050 |
|---|
| 36 | 1.3016 |
|---|
| 37 | 1.2603 |
|---|
| 38 | 1.2296 |
|---|